COPPER TC TYPE T STD Material #: 100206
Electrical
Physical
- Specific Resistance (Ω–CM/F)
- 10.300
- Specific Resistivity (μ Ω–cm2/cm)
- 1.71
- Commercial Resistance Tolerance (On Sizes below .020)
- 3.00%
- Temperature Coefficient of Resistance (ohms/ohm/Deg. C {0 to 100°C})
- 0.00394
- Thermal EMF vs Copper
- -.014
Physical
- Density (gm/cm3)
- Density(lbs/in3)
- 0.32300
- Youngs Modulus (* 106 PSI)
- 17
- Specific Heat at 20 Deg C (cals/gm)
- 0.092
- Thermal Conductivity (watts/cm/Deg. C)
- 3.910000
- Coefficient of Linear Expansion (X 10-6 in/in Deg. C) Deg. C
- 17.0
- Melting Point °C
- 0.00
- Melting Point °F
- 0.00
Specifications
Capabilities
Composition
- ASTM
- ASTM E-230
Capabilities
- Wire
- YES
- Ribbon
- YES
- Square
- YES
- Insulated
- YES
- Plated
- YES
Composition
- Element
- Cu:
- Min
- 99.9900
- Nominal
- 0.0000
- Max
- 0.0000
Tensile Strength
- UTS Hard:
- 55000
- UTS Stress Relieved:
- 0
- UTS Annealed:
- 30000
- YTS Tensile - Hard:
- 40000
- YTS Tensile - Stress Relieved:
- 0
- YTs Tensile - Annealed
- 10000
Note: All values may vary dependent on specific design and usage
Miscellaneous- Magnetic
- None
- Operating Temp °C
- 300.00
- Operating Temp °F
- 572.00