Technical Data Sheet Chromel®TC Type E - Std
| CALIFORNIA FINE WIRE | Electrical | CALIFORNIA FINE WIRE | |
| Specific Resistance (Ω-CM/F) | 425 | ||
| Specific Resistivity(μΩ-cm²/cm) | 70.7 | ||
| Commercial Resistance Tolerance (On Sizes below .020) | 3.00% | ||
| Commercial Resistance Tolerance (On Sizes above .020) | 5.00% | ||
| Temperature Coefficient of Resistance (ohms/ohm/Deg. C {0 to 100°C}) | .000324 | ||
| Thermal EMF vs Copper |
| ||
| CALIFORNIA FINE WIRE | Physical | CALIFORNIA FINE WIRE | |
| Density (gm/cm³ ) | 8.73 | Tensile Strength: | |
| Density(lbs/in³) | 0.3154 | UTS Hard: |
|
| Youngs Modulus (* 106 PSI) |
| UTS Stress Relieved: |
|
| UTS Annealed: | 95,000 | ||
| Specific Heat at 20 Deg C (cals./gm) | 0.107 | YTS Tensile - Hard: |
|
| YTS Tensile - Stress Relieved: |
| ||
| Thermal Conductivity (watts/cm/Deg. C) | 0.192 | YTS Tensile - Annealed: |
|
| Note: All values may vary dependant on specific design and usage | |||
| Coefficient of Linear Expansion (X 10-6 in/in Deg. C) Deg. C | 7.3 | ||
| Melting Point C | 1427 | ||
| Melting Point °F | 2600 | ||
| CALIFORNIA FINE WIRE | Miscellaneous | CALIFORNIA FINE WIRE | ||
| Magnetic | None | |||
| Operating Temp C | 1093 | Composition | ||
| Operating Temp °F | 2000 | Nickel | 90 | |
| Specifications: | Chromium | 10 | ||
| ASTM-E-230 |
|
| ||
|
|
|
| ||
|
|
|
| ||
| Capabilities | ® Registered trade name of Hoskins Manufacturing VISIT US ON THE INTERNET http://www.calfinewire.com | |||
| Wire | YES | |||
| Ribbon | YES | |||
| Square | YES | |||
| Insulated | YES | |||
| Plated | YES | |||